Vibra-Tite 932 Technical Data

Technical Data Sheet

Vibra-Tite® 932

Epoxy

November 2012

Product Description

Vibra-TITE 932 is two-part epoxy encapsulant and
adhesive. This system forms a resilient, long work
time potting and encapsulant material with an easy
mix ratio and good adhesion to thermoplastics. It
will cure rapidly with heat to produce a material with
excellent chemical, heat, and moisture resistance.

Features and Benefits

 Easy mix Ratio
 Excellent chemical resistance
 Excellent dielectric properties
 Casting can survive harsh chemical

exposure

Properties of Uncured Material (resin)

Chemical Type Epoxy
Appearance Black Liquid
Specific Gravity 1.61
Toxicity Low
Solids 100%
Viscosity @ 25ºC, cP 30,000

Properties of Uncured Material
(hardener)

Chemical Type Amine
Appearance Amber Liquid
Specific Gravity 0.98
Toxicity Low
Solids 100%
Viscosity @ 25ºC, cP 1,000

Properties of Cured Material

Vo. Mix Ratio, Resin: Hardener 2 to 1
Wt. Mix Ratio, Resin: Hardener 100:30
Viscosity @ 25ºC, cP 5,800
Work Time, 100g (25ºC) 40-50 mins
Gel Time, 100g (25ºC) 70-90 mins
Regular Cure Schedule (25ºC) 24 hrs
Alternate Cure Schedule (66 ºC) 2 hours
Glass Transition Temp., °C 50
Linear Shrinkage,(cm/cm) 0.002
CTE below Tg, (mm/mm °C) 52.6 E-.06
Hardness @ 25ºC , Shore D 85

Electrical Properties

Dielectric Constant, ASTM D150

0.1 kHz 3.59

1.0 kHz 3.50
10 kHz 3.48
100 kHz 3.38

Dissipation Factor, ASTM D150

0.1 kHz .01

1.0 kHz .01
10 kHz .01
100 kHz .01

Volume Resistivity
@25°C 3.4x1014 Ohm-cm

@130°C 8.3x10

10

Ohm-cm

General Information

Storage

Product should be stored in cool, dry conditions.
VIBRA-TITE 932 when un-mixed has a shelf life of
12 months when stored at 25°C. Storage in cool,
clean areas is recommended. Usable shelf life may
vary depending on method of applications and
storage conditions.

Note

The data are furnished for information only and are
believed to be reliable. We cannot assume
responsibility for the results obtained by others over
whose methods we have no control. It is
recommended that the product be tested in the
application for which it is to be used.