Page 1
Cyanoacrylate
Product Description
Base Compound
Ethoxyethyl
Cyanoacrylate
Appearance
Black Liquid
Viscosity (cP @ 68°F)
2500 cP
Specific Gravity (g/cc)
1.05
Flash Point (TCC)
176°F
Shelf Life @40°F
1 year unopened
°
Steel
40 to 60 seconds
Aluminum
20 to 30 seconds
Neoprene
< 20 seconds
ABS
20 to 30 seconds
Polycarbonate
30 to 45 seconds
PVC
30 to 50 seconds
Polymer (Cured)
Appearance
Colorless Solid
Service Temperature
Range
Softening Point
Refractive Index
1.49
Full Cure Time
24 Hours
Dielectric Strength
(KV/mm)
12.6
Dielectric Constant
(@ 1Kc)
5.4
COE (in./in./F)
.000126
Tensile Strength
2300 psi
T-peel strength
12 lbs/inch
Solubility
Nitromethane,
Substrate
Range in N/mm2
Blasted Steel
16 to 20
Etched Aluminum
11 to 18
Neoprene
> 10
ABS
>6
Polycarbonate
>5
PVC
>6
Strength at Temperature
0.00
20.00
40.00
60.00
80.00
100.00
0 60 80 100 120
Temperature , C
% Retained
318
Vibra-TITE 318 is a single component, rubbertoughened cyanoacrylate adhesive. No-odor and nonblooming characteristics make this product user friendly
when vapor control is an issue. It is specially designed
for applications needing higher peel strength.
Monomer (Liquid)
Curing Properties
Ambient surface moisture will initiate the hardening
process. Handling strength is reached in a short period
of time and varies depending on environmental
conditions and substrates being bonded. Product will
continue to cure for at least 24 hours before full strength
and resistances are developed.
Physical Properties
Product Data Sheet
-65°F to 200°F
293°F
(ND 20)
(steel/steel)
Acetone,
Dimethylformamide
Performance of Cured Materials
Tensile Shear strength after 48 hours at 20° to 25°C
Setting Time (68
Curing Performance
The gap of the bond line will affect set speed. Smaller
gaps tend to increase the speed. Activators can be
applied to improve set speed but may also impair overall
adhesive performance.
F, 65% R.H.)
Temperature Resistance
Sheer Strength on steel after 1 week at 22 °C
Page 2
Cyanoacrylate
Chemical Resistance
% Strength Retained
Motor Oil
100
Gasoline
100
Tricloroethane
100
Freon TA
100
10% NaOH
0
10% Hcl
0
Water
0
For safe handling information on this product,
F pr ovides opt imum storage
se. P roducts like i sopropyl a lcohol c an be u sed.
object (such as a teaspoon handle.) In case of eye
contact, b athe i mmediately with water a nd s eek
318
Sheer strength on steel after 12 month soak
Solvent
General Instructions
Surfaces to be bonded should be clean and dry.
Dispense a drop or drops to one surface only. Apply only
enough to leave a thin film layer after compression.
Press parts together and hold firmly for a few seconds.
Good contact is essential. An adequate bond develops in
less that one minute and maximum strength is attained in 24
hours.
Wipe off excess adhesive from the top of the container and
recap. Cyanoacrylate products if left uncapped may
deteriorate by contamination from moisture in the air.
Because Cyanoacrylate products cure by polymerization,
whitening may appear on the surface of the container or the
bonded materials. Should this happen, wipe surfaces well
with acetone.
Product Data Sheet
consult the Material Safety Data Sheet, (MSDS)
General Information
Storage
Refrigeration at 4 0°
stability.
Note
Prior to use, remove all surface contaminants such as oil
or grea
Test compatibility of cleaner with substrate.
Make sure surface is completely dry before bonding.
Health & Safety in use
CAUTION: SuperGlues b ond skin and eyes on contact.
If accidental skin bonding occurs, wash area with warm
soapy water a nd s lowly p ry s kin a part us ing a b lunt
immediate medical attention.
Loading...