Page 1
Cyanoacrylate
Product Description
Base Compound
Ethoxyethyl
Cyanoacrylate
Appearance
Colorless Liquid
68°F)
Specific Gravity
(g/cc)
1.05
Flash Point (TCC)
176°F
Shelf Life @40°F
°
Steel
40 to 60 seconds
Aluminum
20 to 30 seconds
Neoprene
< 20 seconds
ABS
20 to 30 seconds
Polycarbonate
30 to 45 seconds
PVC
30 to 50 seconds
Polymer (Cured)
Appearance
Colorless Solid
Range
293°F
Refractive Index
(ND 20)
1.49
Full Cure Time
24 Hours
Dielectric Strength
(KV/mm)
12.6
Dielectric Constant
(@ 1Kc)
5.4
COE (in./in./F)
.000126
Tensile Strength
2300 psi
T-peel strength
12 lbs/inch
Solubility
Nitromethane,
Dimethylformamide
Substrate
Range in N/mm2
Blasted Steel
16 to 20
Etched Aluminum
11 to 18
Neoprene
> 10
ABS
>6
Polycarbonate
>5
PVC
>6
Strength at Temperature
0.00
20.00
40.00
60.00
80.00
100.00
0 60 80 100 120
Temperature , C
% Retained
317
Vibra-TITE 317 is a single component, rubbertoughened cyanoacrylate adhesive. No-odor and
non-blooming characteristics make this product
user friendly when vapor control is an issue. It is
specially designed for applications needing higher
peel strength.
Monomer (Liquid)
Viscosity (cP @
Curing Properties
Ambient surface moisture will initiate the hardening
process. Handling strength is reached in a short
period of time and varies depending on
environmental conditions and substrates being
bonded. Product will continue to cure for at least
24 hours before full strength and resistances are
developed.
Setting Time (68
Physical Properties
2500 cP
1 year unopened
F, 65% R.H.)
Product Data Sheet
Service Temperature
Softening Point
(steel/steel)
Performance of Cured Materials
Tensile Shear strength after 48 hours at 20° to 25°C
Temperature Resistance
Sheer Strength on steel after 1 week at 22 °C
-65°F to 200°F
Acetone,
Curing Performance
The gap of the bond line will affect set speed.
Smaller gaps tend to increase the speed.
Activators can be applied to improve set speed but
may also impair overall adhesive performance.
Page 2
Cyanoacrylate
Chemical Resistance
% Strength Retained
Motor Oil
100
Gasoline
100
Tricloroethane
100
Freon TA
100
10% NaOH
0
10% Hcl
0
Water
0
For safe handling information on this product,
F pr ovides opt imum storage
object (such as a teaspoon handle.) In case of eye
contact, b athe i mmediately with water a nd s eek
317
Sheer strength on steel after 12 month soak
Solvent
General Instructions
Surfaces to be bonded should be clean and dry.
Dispense a drop or drops to one surface only. Apply only
enough to leave a thin film layer after compression.
Press parts together and hold firmly for a few seconds.
Good contact is essential. An adequate bond develops in
less that one minute and maximum strength is attained in 24
hours.
Wipe off excess adhesive from the top of the container and
recap. Cyanoacrylate products if left uncapped may
deteriorate by contamination from moisture in the air.
Because Cyanoacrylate products cure by polymerization,
whitening may appear on the surface of the container or the
bonded materials. Should this happen, wipe surfaces well
with acetone.
Product Data Sheet
consult the Material Safety Data Sheet, (MSDS)
General Information
Storage
Refrigeration at 4 0°
stability.
Note
Prior to use, remove all surface contaminants such as oil
or grease. P roducts l ike i sopropyl al cohol ca n b e u sed.
Test compatibility of cleaner with substrate.
Make sure surface is completely dry before bonding.
Health & Safety in use
CAUTION: SuperGlues bond skin and e yes on c ontact.
If accidental skin bonding occurs, wash area with warm
soapy water a nd s lowly p ry s kin a part us ing a b lunt
immediate medical attention.
Loading...