3M 4943F DATA SHEET

VHB Acrylic Foam Tape 4943F
Product Data Sheet
Updated : Sept. 2002 Supersedes : May 2002
Product Description
4943 is a conformable, very high bond acrylic foam tape which has added performance for bonding at low temperatures (above 0 °C). In addition this adhesive composition makes the product well suited to a variety of substrates. Its improved conformability also allows more complete bond contact area when bonding rigid or irregular materials. 4943's principal advantage is that it provides a more uniform seal on irregular surfaces. Resistance to solvents, temperature extremes and U.V. light make VHB products suitable for many interior and exterior applications.
Physical Properties
Not for specification purposes
Adhesive Type
Acrylic
Thickness (ASTM D-3652)
Tape Liner Total
1.1 mm ± 10%
0.05 mm
1.15 mm
Foam Density
720 k/gm³
Release Liner
Clear Film
Tape Colour
Grey
Shelf Life
24 months from date of despatch by 3M when stored in the original carton at 20°C & 50 % Relative Humidity
Performance Characteristics
Not for specification purposes
Peel Adhesion to Stainless Steel
90° peel @ room temp, 72 hr dwell, jaw speed 300mm/min
44.0 N/10mm
Static Shear Strength
weight held for 10,000 mins to stainless steel with ½ sq in (3.23 sq cm) overlap
1000 g @ 20°C 500 g @ 70°C
Normal Tensile (T­Block)
to Aluminium at room temp,
6.45 sq cm, jaw speed 50 mm/min
585 kPa
2
Date : Sept. 2002 VHB Acrylic Foam Tape 4943F
Performance Characteristics (Cont...)
Not for specification purposes
Temperature Performance
(Minutes/Hours) (Days/Weeks)
150 °C
90 °C
Solvent Resistance
Splash testing cycle - 20 seconds submersion
- 3 cycles.
No apparent degradation when exposed to splash testing of most solvents including gasoline, JP-4 jet fuel, mineral spirits, motor oil, ammonia cleaner, acetone, methyl ethyl ketone. 20 seconds air dry.
UV Light Resistance
Excellent.
Additional Product Information
Bond strength is dependent upon the amount of adhesive-to-surface contact developed. Firm application pressure develops better adhesive contact and thus improves bond strength.
To obtain optimum adhesion, the bonding surfaces must be clean, dry and well unified. Typical surface cleaning solvents are isopropyl alcohol/water mixture (rubbing alcohol) or heptane. Use proper safety precautions for handling solvents.
It may be necessary to seal or prime some substrates prior to bonding.
a. Most porous or fibred materials (e.g. wood) will require sealing to provide a unified
surface.
b. Some materials (e.g. copper, brass, plasticised vinyl) will require priming or
coating to prevent interaction between adhesive and substrates.
Acrylic Foam Tape 4943F utilises a unique low temperature acrylic adhesive which allows initial applications to be made at temperatures as low as 0°C.
At room temperature the adhesive is very aggressive and provides excellent initial adhesion to many surfaces.
Low temperature application.
Most high performance pressure sensitive acrylic adhesives have very low initial tack at temperatures below 0°C. Acrylic Foam Tape 4943F was designed to allow outdoor assembly of signs and construction materials and assembly of cold materials in large manufacturing plants above 0°C.
Room temperature applications.
At room temperature 4943F offers better tack/quick stick than other tapes in the VHB family. This can be important in a wide range of applications where a more aggressive adhesive is desirable.