Page 1
Operating Instructions
Stand of the operating instructions: 11/2009
General terms: SOLIBOND C plus is a clinical proved berylium free Cobalt-Chrome Alloy.
1.1. Product description/ Art. 969-0250 SOLIBOND C plus 250 g
Delivery: Art. 969-1000 SOLIBOND C plus 1000 g
1.2. Manufacturer: YETI Dentalprodukte GmbH, Industriestraße 3, D-78234 Engen, Germany
Tel. : 07733-94100 Fax: 07733-941022 e-mail-adresse: [email protected]
Technical Questions: 07733-9410-20
2. Determined use:
Biocompatible Cobalt-Chrome dental alloy with less oxide film, to be used only by dental techniciansor similarly qualified
people for dental restorations in the patient’s mouth.
3. Instructions for useitungsanleitung:
3.1 Modelling
The wall thickness of of the modelling units should not be less than 0,35 mm. Please ensure that sprues with the right
dimensions (thickness & reservoir) are attached to the full cast crown and bridge parts.
3.2. Bedding
SOLIBOND C plus i
bound commercial investments which can be pre-heated up to 900°C following the manufacturers instructions. A
setting time of 30 minutes has proved to be good at the praxis.
3.3. Casting
SOLIBOND C plus must be melted in a ceramic crucible under steamer pressure. Never use graphite crucibles. Use
always the same alloy with the same crucible and clean after use.
Flame melting and The neutral adjusted flame with Propan/Oxygen or Azetylen/Oxygen in addition to the
high frequency non use of the Flux prevents overheating of the alloy. As soon as the last cast ingots have
slumped and approximately 2 seconds after disappearance of the shade, start the casting
procedure after the tear of the oxide layer.
3.4. Cool
After casting let the muffle cool slowly and at room temperature, (do not rinse with cold water). Please note that reuse
of the cast metal is not recommended as important ingredients for metal/ceramic bonding will evaporate through the
melting of the alloy. During repeated re-melting, these components decrease and a sufficient metal/ceramic bonding can
no longer be guaranteed. The units are finished using normal tungsten carbides and aluminium-oxide stones. The
minimum thickness of the finished units should be 0,2 mm. To avoid any contamination while working with different alloys,
we suggest you use the same grinding instruments.
3.5. Ceramic burn
Oxide burning can be done at 960°C for 5 minutes. Next, blast frames with 100-25 0my Aluminium oxide and
clean as usual with distilled water, ultrasonic or steam cleaner. Never strip non precious metal to ceramic
alloys. Please process the WAK (coefficient of expansion) wash and opaque burning according to ceramic
processing instructions. Effect long-term cooling with Dentine, corrections and glaze burning up to aprox.
750°C, but which is not necessary with K2 LF or PoM (Press over Metal).
4.0 Soldering
SOLIBOND C can be soldered with LOT UNIVERSAL Art. 960-0000. Do not use Gold or Palladium soldering
Materials.
5.0 Guarantee and safety indications
metal powder is dangerous fot healthy and its processing should only be done under the exhauster. Please consider
hypersensitive reaction to elements of the alloy. Our liability for the correctness of this information is independent of the
legal ground and, in as far as legally permissible, is limites to the invoiced value of the goods supplied excluding turnover
tax.
1253
Solibond C plus corresponds to the requirements of DIN EN ISO 22674 and points
out due to its hardness of 280 HV10.
SOLIBOND C plus is suitable for open flame melting as well as for high frequency
casting. One of its remarkable features is its ability to be scanned by laser and its high
biocompatibility.
s compatible with YETIVEST Art. 932-0000 or Duovest Art. 952-0000 or any other phosphate-
YETI Dentalprodukte GmbH
Industriestr. 3 78234 Engen, Germany
Telefon 07733-9410 0 Fax 07733-9410 22
Internet: www.yeti-dental.com - www.dentalwax.com
Page 2
Operating Instructions
1253
Stand of the operating instructions: 11/2009
Certificate
Produkt’s name: SOLIBOND C plus
Description:
Delivery: 250 gr Art. No. 969- 0250
1000 gr Art. No. 969- 1000
Chemical Composition according to: EN 10204 – 2.2
Co % Cr % W % Mo %
Metal to ceramic Co Cr Dental Alloy
Nb %
Si %
63
24 8,1 2,9 0,9 1,1
Technical Data:
Density:
Melting point (Solidus/Liquidus):
Casting temperature
Coefficient of Expansion (20-600° C):
Hardness:
Modul of Elasticity:
Expansion :
0,2% Expansion limit: 550
Norm: DIN EN ISO 9693
DIN EN ISO 22674
Alloys Typ 2-4
8,3 g/cm³
1.310 – 1.370°C
1.430 °C
14,0 x 10
280 HV
210.000 Mpa
10,1 %
550 MPa
-6
YETI Dentalprodukte GmbH
Industriestr. 3 78234 Engen, Germany
Telefon 07733-9410 0 Fax 07733-9410 22
Internet: www.yeti-dental.com - www.dentalwax.com