Technical Data Sheet
Vibra-Tite® 560
Retaining Compound
September 2012
Product Description
Vibra-Tite 560 is a high strength, high temperature,
anaerobic retaining compound used for bonding rigid
assemblies of all types. This material can be used
effectively to increase the strength of most
mechanical assemblies.
Typical Applications
Vibra-TITE 560 performs on aluminum, steel, plated,
stainless steel, and special alloy parts. Locks shaft
and hubs together for ears, bearing, bushings. Bonds
pins, adaptors, plugs.
Instructions for Use
Ensure parts are clean, dry and free from oil and
grease.
Procedure for Application
Product is normally hand applied from the bottle onto
parts.
Compatible Primers
Primers such as Vibra-TITE Excel 611 (Primer N) or
Vibra-TITE 612 (Primer T) can be used. The use of
primers can cause loss of strength and performance
should be tested.
Technical Features
Resin:..................................Dimethylacrylate
Color:....................................Green
Fixture Speed w/Primer……<5 minutes
Fixture Speed w/out Primer..10 min. @ 68°F
Viscosity………………............600 cps
Gap Fill......................................0.007"
Max. Operating Temp….-65°F to +400°F
Cured Performance
Full Cure Time.................24 hours @ 68°F
Shear Strength………………>3000 psi
Presentation
Bottles….......10ml, 50ml, 250ml and liter
General Information
Storage
Product should be stored in a cool and dry location at
temperatures between 14°F (-10°C) to 86°F (30°C).
Shelf life is 2 years from date of manufacture when
stored at 72±8°F (22±4°C).
Note
Vibra-TITE 560 is a low viscosity rapid curing liquid
which augments press fit and slip fit applications.
Product conforms to MIL-R-46082 and ASTM D-
5363.
Health & Safety in use
IRRITANT: Contains Methacrylate Esters which
may irritate eyes, respiratory organs and skin. In
case of contact with the skin, wash immediately
with plenty of water.