Page 1
Cyanoacrylate
Product Description
Appearance
Colorless Liquid
Viscosity (cP @ 68°F)
500 cP
Specific Gravity (g/cc)
1.06
185°F
Shelf Life @60°F
Steel
25 to 60 seconds
Aluminum
25 to 50 seconds
Neoprene
20 to 40 seconds
ABS
25 to 50 seconds
Polycarbonate
40 to 80 seconds
PVC
20 to 38 seconds
Polymer (Cured)
Appearance
Colorless Solid
Range
Softening Point
329°F
Refractive Index
(ND 20)
1.49
Full Cure Time
24 Hours
Dielectric Strength
(KV/mm)
11.6
Dielectric Constant
5.4
COE (in./in./F)
.000126
Tensile Strength
(steel/steel)
3700 psi
Solubility
Nitromethane,
Substrate
Range in N/mm2
Blasted Steel
20 to 28
Etched Aluminum
14 to 23
ABS
> 6
Polycarbonate
> 5
PVC
> 6
Strength at Temperature
0.00
20.00
40.00
60.00
80.00
100.00
0 60 80 100 120
Temperature , C
% Retained
335
Vibra-TITE 335 is medium viscosity, rubbertoughened ethyl cyanoacrylate adhesive. Provides
superior shock and thermal resistance when
bonding rubbers, metals, and plastics in harsh
environments.
Monomer (Liquid)
Base Compound Ethyl Cyanoacrylate
Flash Point (TCC)
Military Specifications
Mil-A-46050C
Type II, Class 2
Curing Properties
Ambient surface moisture will initiate the hardening
process. Handling strength is reached in a short period
of time and varies depending on environmental
conditions and substrates being bonded. Product will
continue to cure for at least 24 hours before full strength
and resistances are developed.
Physical Properties
6 months unopened
Product Data Sheet
Service Temperature
(@ 1Kc)
Performance of Cured Materials
Tensile Shear strength after 48 hours at 20° to 25°C
Neoprene > 10
Temperature Resistance
Sheer Strength on steel after 1 week at 22 °C
-65°F to 280°F
Acetone,
Dimethylformamide
Setting Time (68°F, 65% R.H.)
Curing Performance
The gap of the bond line will affect set speed. Smaller
gaps tend to increase the speed. Activators can be
applied to improve set speed but may also impair overall
adhesive performance.
Page 2
Cyanoacrylate
Chemical Resistance
% Strength Retained
Motor Oil
100
Gasoline
100
Tricloroethane
100
Freon TA
100
10% NaOH
0
10% Hcl
0
Water
0
For safe handling information on this product,
ct fr om
or g rease. P roducts like isopropyl alcohol c an be u sed.
object (such as a teaspoon handle.) In case of eye
he i mmediately with water a nd s eek
335
Sheer strength on steel after 12 month soak
Solvent
General Instructions
Surfaces to be bonded should be clean and dry.
Dispense a drop or drops to one surface only. Apply only
enough to leave a thin film layer after compression.
Press parts together and hold firmly for a few seconds.
Good contact is essential. An adequate bond develops in
less that one minute and maximum strength is attained in 24
hours.
Wipe off excess adhesive from the top of the container and
recap. Cyanoacrylate products if left uncapped may
deteriorate by contamination from moisture in the air.
Because Cyanoacrylate products cure by polymerization,
whitening may appear on the surface of the container or the
bonded materials. Should this happen, wipe surfaces well
with acetone.
Product Data Sheet
consult the Material Safety Data Sheet, (MSDS)
General Information
Storage
Products should be stored unopened in a cool, dry place
out of direct sunlight. Products should be kept at room
temperature a way from d irect lig ht. P rote
extreme heat or cold, do not refrigerate.
Note
Prior to use, remove all surface contaminants such as oil
Test compatibility of cleaner with substrate.
Make sure surface is completely dry before bonding.
Health & Safety in use
CAUTION: SuperGlues bond skin and e yes o n c ontact.
If acci dental s kin bonding occurs, wash area with warm
soapy water a nd s lowly p ry s kin a part us ing a b lunt
contact, b at
immediate medical attention.
Loading...