Cyanoacrylate
Product Description
Base Compound
Ethyl Cyanoacrylate
Appearance
Colorless Liquid
Viscosity (cP @ 68°F)
800 cP
Specific Gravity (g/cc)
1.06
Flash Point (TCC)
185°F
Shelf Li fe @40°F
1 year unopened
°
Steel
10 to 20 seconds
Aluminum
7 to 15 seconds
Neoprene
< 7 seconds
ABS
5 to 10 seconds
Polycarbonate
10 to15 seconds
PVC
5 to 10 seconds
Polymer (Cured)
Appearance
Colorless Solid
Service Temperature
Range
Softening Point
Refractive Index
1.49
Full Cure T ime
24 Hours
Dielectric Strength
(KV/mm)
11.6
Dielectric Constant
(@ 1Kc)
5.4
COE (in./in./F)
.000126
Tensile Str ength
3400 psi
Solubility
Nitromethane,
Dimethylformamide
Substrate
Range in N/mm2
Blasted Steel
19 to 25
Etched Aluminum
12 to 20
Neoprene
> 10
ABS
> 6
Polycarbonate
> 5
PVC
> 6
Strength at Temperature
0.00
20.00
40.00
60.00
80.00
100.00
0 60 80 100 120
Temperature , C
% Retained
331
Vibra-TITE 331 is a single component medium viscosity
cyanoacrylate adhesive. Suitable for general-purpose
bonding but provides excellent strength and speed on all
rubber compounds.
Monomer (Liquid)
Military Specifications
Mil-A-46050C
Type II, Class 3
Curing Properties
Ambient surface moisture will initiate the hardening
process. Handling strength is reached in a short period
of time and varies depending on environmental
conditions and substrates being bonded. Product will
continue to cure for at least 24 hours before full strength
and resistances are developed.
Physical Properties
Product Data Sheet
-65°F to 200°F
329°F
(ND 20)
(steel/steel)
Acetone,
Performance of Cured Materials
Tensile Shea r strength after 48 hours at 20° to 25°C
Setting Time (68
Curing Performance
The gap of the bond line will affect set speed. Smaller
gaps tend to increase the speed. Activators can be
applied to improve set speed but may also impair overall
adhesive performance.
F, 65% R.H.)
Temperature Resistance
Sheer Stre ngth on steel after 1 week at 22 °C
Technical data contained within this document is intended for reference only
For assistance and recommendations on specifications for this product, contact ND Industries