Garlock 3510 User Manual
MATERIAL PROPERTIES
*
Color:
Composition:
Fluid Services
1
:
Temperature
2
Minimum: -450 (-268)
Pressure
2
P x T (max.)
2
Flammability
Bacterial Growth
Meets Specification:
PHYSICAL PROPERTIES
*
ASTM F36
Compressibility
ASTM F36
Recovery
ASTM F38
Creep Relaxation
Tensile
ASTM D792
Specific Gravity
ASTM D1708
Modulus @ 100% Elongation
ASTM F433
Thermal Conductivity (K)
ASTM D149
Dielectric Properties
(3)
ASTM F586
Design Factors
Gasket Constants
-11
-2
Line Call Out
(4)
SEALING CHARACTERISTICS
*
Gasket Load
Internal Pressure
Leakage
0.04 ml/hr.
<0.015 cc/min
Continuous Max: +500 (+260)
1/32 and 1/16": 350,000 (12,000)
1/8": 250,000 (8,600)
ASTM F152
ROTT
ASTM F104
Garlock GYLON®3510
Off White
PTFE with barium sulfate
Strong caustics, moderate acids, chlorine, gases, water, steam, cryogenics,
hydrocarbons and aluminum fluoride
, °F (°C)
, Maximum, psig (bar): 1200 (83)
, psig x °F (bar x °C)
: Will Not Burn
: Will Not Support
ABS (American Bureau of Shipping) and FDA (Food and Drug Administration)
, %: 4-10
, %: 40
, %: 11
, Across Grain, psi (N/mm2): 2000 (13.8)
: 2.80
, range, volts/mil.
Sample conditioning 1/16" 1/8"
3 hours at 250°F: 466
96 hours at 100% Relative Humidity 59 -
"m" factor: 2.0 2.0
"y" factor, psi (N/mm2):
, 1/16": Gb=289 a=0.274
1/8": Gb=444 a=0.332
:
, psi (N/mm2): 1400 (9.6)
, W/m°K (Btu.·in./hr.·ft.
2
·°F): 0.29-0.38 (2.00-2.65)
1/16" 1/8"
2350 (16.2) 2500 (17.2)
F451999A9B2E99K5M6
-
Gs=6.61x10
Gs=1.29x10
Notes:
This is a general guide and should not be the sole means of selecting or rejecting this material. ASTM test results in accordance with ASTM F-104;
properties based on 1/32" (0.8mm) sheet thickness unless otherwise mentioned.
* Values do not constitute specification Limits
1
See Garlock chemical resistance guide.
2
Based on ANSI RF flanges at our preferred torque. When approaching maximum pressure, continuous operating temperature, minimum temperature or
50% of maximum PxT, consult Garlock Applications Engineering.
3
Indicates current arced around and not through gasket. Dielectric higher than indicated.
4
Increase in IRM Oil #903 (fourth numeral 9 is thickness, fifth numeral 9 is weight): Thickness = 1.0% max, Weight = 2.0% max. Sixth numberal 9: %
Increase in Water: Weight = 1.0% max. A9: Leakage in Fuel A (Isooctane), Pressure = 9.8psig (0.7bar), Gasket Load = 1,000psi (7.0N/mm2): Typical =
0.04ml/hr, Max = 1.0ml/hr. E99: % Increase in ASTM Fuel B: Weight: 2.0% max., Thickness: 1.0% max.
, psi (N/mm2):
, psig (bar):
ASTM F37B DIN 3535- 4
Fuel A Gas Permeability
1000 (7) 4640 (32)
9.8 (0.7) 580 (40)