futura ReForm - rPLA Technical Data Sheet

Formfutura BV CoC: 69099502 Tel: [phone]

Groenestraat 215 VAT: NL857733709B01 Email: [e-mail]

6531 HH Nijmegen EORI: NL857733709 Website: www.formfutura.com

The Netherlands

ReForm is a sustainable initiative within Formfutura to efficiently manage residual extrusion waste streams and re-use them
into high-end upcycled filaments. The ideology behind ReForm is to a make 3D printing more sustainable – without having

to make compromises on material properties – and yet keep it affordable.

ReForm rPLA is based on exactly the same unique formulation as our EasyFil PLA range, but is made out of residual
extrusion waste streams which are re-compounded and homogenized into a high-end and easy to print upcycled PLA
filament with significant less environmental impact.

All information supplied by or on behalf of Formfutu ra in relation to its products, whether in the nature of data, recommendations or otherwise, is supported by research and, in good faith,
believed reliable, but Formfutura assumes no liability and makes no warrant ies of any kind, express or implied, including, but not limited to, those of tit le, merchantability, fitness for a
particular purpose or non-infringement or any warranty arising from a course of dealing, usage, or trade practice whatsoever in respect of application, processing or use made of the
forementioned information or product. The user assumes all responsibility for the use of all information provided and shall verify quality and other propertie s or any consequence from the use
of all such information. Typical values are indicative only and are not to be construed as being binding specifications.

≥ 95%

± 0.10mm

HS Code

REACH compliant

RoHS certified

-

Mechanical

Impact strength

7.5 KJ/m²

-

Tensile modulus

Tensile strength

110 Mpa (MD)

ASTM D882

---

Flexural modulus

± 2392.5 Mpa

-

-

Technical Data Sheet

Product name:

ReForm™ - rPLA

Version:

v3

Water absorption

---

Physical

Specific gravity

1.24 g/cc

ASTM D1505

-

Melt flow rate

6.0 g/10min

-

-

Properties

Typical value

Test Method

Test condition

Moisture absorption

---

Hardness

---

Thermal

3310 Mpa (MD)

ASTM D882

-

Elongation at break

160% (MD)

ASTM D882

-

Flexural strength

± 55.2 Mpa

Print temperature

± 180 - 220° C

---

Melting termperature

± 210 ± 10° C

--Viscat softening temp.

± 60° C

ISO 306

-

39169090

Yes

Yes

Product details, certifications and compliance

2.85mm

Optical

Haze

2.1%

ASTM D1003

Diameter

Tolerance

Roundness

≥ 95%

± 0.05mm

1.75mm

-

Gloss

90

ASTM D1003

Gloss, 20°

Transmittance

-

-