Page 1
SPECIFICATION
••••
Supplier : Samsung electro-mechanics •••• Samsung P/N :
•••• Product : Multi-layer Ceramic Capacitor •••• Description :
A. Samsung Part Number
CL 21 C 220 J B A N N N C
①①①① ②②②② ③③③③ ④④④④ ⑤⑤⑤⑤ ⑥⑥⑥⑥ ⑦⑦⑦⑦ ⑧⑧⑧⑧ ⑨⑨⑨⑨ ⑩⑩⑩⑩ ⑪⑪⑪⑪
①①①① Series
②②②② Size
③③③③ Dielectric
④④④④ Capacitance
⑤⑤⑤⑤ Capacitance
tolerance ⑨⑨⑨⑨ Product
⑥⑥⑥⑥ Rated Voltage
⑦⑦⑦⑦ Thickness
B. Samsung Reliablility Test and Judgement condition
Samsung Multi-layer Ceramic Capacitor
0805 (inch code) L: 2.0 ± 0.1 mm W: ± 0.1 mm
C0G
22
㎊
±5
%
50 V
0.65 ± 0.1 mm
⑧⑧⑧⑧ Inner electrode
Termination
Plating
⑩⑩⑩⑩ Special
⑪⑪⑪⑪ Packaging
CL21C220JBANNNC
CAP, 22㎊㎊㎊㎊, 50V, ±5%, C0G, 0805
1.25
Ni
Cu
Sn 100%
Normal
Reserved for future use
Cardboard Type, 7" reel
(Pb Free)
Capacitance
Q
Insulation
Resistance
Appearance
Withstanding
Voltage
Temperature
Characterisitcs
Adhesive Strength
of Termination
Bending Strength
Solderability
Resistance to
Soldering heat
Performance Test condition
Within specified tolerance
840 min
10,000Mohm or 500Mohm⋅㎌
Whichever is Smaller
No abnormal exterior appearance
No dielectric breakdown or of the rated voltage
mechanical breakdown
C0G
(From -55℃ to 125℃, Capacitance change shoud be within ±30PPM/℃)
No peeling shall be occur on the
terminal electrode
Capacitance change : Bending to the limit (1mm)
within ±5% or ±0.5㎊ whichever is larger
More than 75% of terminal surface SnAg3.0Cu0.5 solder
is to be soldered newly
Capacitance change :
within ±2.5% or ±0.25㎊ whichever is larger
Tan δ, IR : initial spec.
1㎒±10%
Rated Voltage 60~120 sec.
Microscope (×10)
300%
500g⋅F, for 10±1 sec.
with 1.0mm/sec.
245±5℃, 3±0.3sec.
(preheating : 80~120℃ for 10~30sec.)
Solder pot : 270±5℃, 10±1sec.
0.5~5Vrms
Page 2
Vibration Test
With
Min. operating temperature
Moisture
Resistance
High Temperature
Resistance
Temperature
Cycling
Performance Test condition
Capacitance change : Amplitude : 1.5mm
within ±2.5% or ±0.25㎊ whichever is larger From 10㎐ to 55㎐ (return : 1min.)
Tan δ, IR : initial spec.
Capacitance change : With rated voltage
within ±7.5% or ±0.75㎊ whichever is larger 40±2℃, 90~95%RH, 500+12/-0hrs
Q : 173.33 min
IR :
Whichever is Smaller
Capacitance change :
within ±3% or ±0.3㎊ whichever is larger
Q : 330 min 1000+48/-0hrs
IR :
Whichever is Smaller
Capacitance change : 1 cycle condition
within ±2.5% or ±0.25㎊ whichever is larger
Tan δ, IR : initial spec.
500Mohm or 25Mohm ⋅ ㎌
1000Mohm or 50Mohm ⋅ ㎌
2hours × 3 direction (x, y, z)
200%
Max. operating temperature
Max. operating temperature
→
5 cycle test
of the rated voltage
→
25℃
→
25℃
C. Recommended Soldering method :
Reflow ( Reflow Peak Temperature : 260+0/-5℃, 10sec. Max )
* For the more detail Specification, Please refer to the Samsung MLCC catalogue.